Abstract
Coordination polymers of metal-croconate (C5O52−) complex, {[Ni2(bpe)2(C5O5)2]·H2O}n (1) (bpe = 1,2-bis(-4-pyridyl)ethylene)) with two-dimensional (2D) metal–organic frameworks (MOF), have been synthesized under hydrothermal conditions and characterized by single-crystal X-ray diffraction studies. Structural determination reveals that compound 1 contains two crystallographically independent Ni(II) ions which both lie in a distorted octahedral environment bonded to two bpe nitrogen atoms and four oxygen donors from two croconates. The croconate acts as a bridging ligand with two different bridging modes, one presents a bis-bidentate adjacent μ3-coordination mode and the other a bis-bidentate μ4-coordination mode. A 2D brick-wall-like layered framework is formed by using a rectangle grid as a basic building unit through the connectivity of NiII with hybrid μ3-, μ4-croconates and bpe ligands. Two layers are then cross-linked by the other bpe ligands to complete a 2D bi-layered MOF. The TGA associated with in situ XRD measurements demonstrated that 1 have quite high thermo-stability that keep their crystalline forms up to 350 °C. Magnetic measurements show the long range magnetic ordering and spin canting behavior in 1 below the critical temperature of 22 K with an approximate canting angle of 0.79°. A large coercivity of 3.5 kOe in the hysteresis loop is observed at 1.8 K, indicating that 1 is a weak hard magnet.The research was conducted at the NSRRC beamline 01C2.
C.-C. Wang, F.-C. Liu, C.-K. Chiu, Y. Song, S.-C. Wang, Y. Wang, G.-H. Lee, H.-S. Sheu, and E.-C. Yang |